Oxide systems with the nominal composition LaCaCuVMnO7.5 and composites modified with the YBa2Cu3Ox phase were synthesized by the solid-state reaction method. The phase composition and structural features were systematically investigated by X-ray diffraction (XRD), Rietveld refinement, and scanning electron microscopy coupled with energy-dispersive X-ray spectroscopy (SEM–EDX). The parent oxide was found to form a two-phase system, consisting of an orthorhombic perovskite-like phase and a cubic manganite–vanadate phase, whereas the introduction of 10 wt.% YBa2Cu3Ox resulted in the formation of a three-phase composite containing an additional cuprate phase. Thermophysical investigations in the 298–673 K range revealed λ-type-like anomalies in the heat capacity, which may be associated with possible structural or interphase transformations in the investigated oxide systems. The incorporation of YBa2Cu3Ox significantly modified the temperature dependence of heat capacity and increased its values over both low- and high-temperature regions. Electrophysical measurements in the 293–483 K range confirmed the semiconducting nature of conductivity, while the addition of YBa2Cu3Ox reduced electrical resistance and enhanced dielectric permittivity. These findings demonstrate that YBa2Cu3Ox modification provides an effective route for tuning the thermophysical and electrophysical properties of LaCaCuVMnO7.5-based oxide systems, suggesting their potential as promising candidates for multifunctional oxide materials with possible electronic and sensor-related applications.