Lead-bearing dusts from metallurgical processes are hazardous secondary resources due to their complex composition and toxicity. At the same time, their high lead content makes them a promising feedstock for resource recovery. This study proposes an energy-efficient electrosmelting approach based on the partial substitution of sodium carbonate with calcium-rich industrial waste (sugar-industry defecate). Thermodynamic analysis and equilibrium modeling of the Pb–Sb–Fe–Na–Ca–Si–S–Cl–As system were performed in the temperature range of 200–1200 °C using Outotec HSC Chemistry. The results indicate that under equilibrium conditions approximately 90–95% of lead is concentrated in the metallic phase (~56 kg from ~60 kg in the feed), while antimony is co-recovered (~1.9–2.0 kg). The slag is dominated by calcium silicates, primarily Ca2SiO4, confirming the important role of CaO in slag formation and impurity fixation. Chlorine is predominantly bound as NaCl and partially as CaCl2, while sulfur is distributed between Na2S and Na2SO4. A significant portion of arsenic is predicted to be retained in the slag as calcium and sodium arsenates (Ca3(AsO4)2 and Na3AsO4), whereas its volatilization is thermodynamically negligible under equilibrium conditions. Preliminary experimental results are generally consistent with the thermodynamic predictions and confirm the feasibility of partially replacing Na2CO3 with sugar-industry defecate. The proposed approach contributes to reducing the consumption of conventional fluxes and promotes the utilization of industrial waste within a circular-economy framework.