This study addresses the problem of efficient utilization of aspiration dust (AD) generated during crushing of high-carbon ferrochrome (HCFeCr). To solve this issue, a briquetting technology was proposed, involving aspiration dust blended with dry gas-cleaning dust (20 wt.% as filler) and an organic polymer binder (3 wt.%). The produced briquettes demonstrated high mechanical strength (average 195 kg per briquette in splitting strength and 98% drop resistance), ensuring maximum integrity during transportation and handling. Pilot-industrial remelting of 35 tons of briquettes in a 1.8 MVA direct current electric arc furnace (DC EAF) confirmed the effectiveness of the proposed technology for HCFeCr production. Chromium recovery into the alloy reached 94%, which is 3-4% higher compared to remelting of loose dust. The specific electric energy consumption was 1600 kWh/t, representing a 29% reduction compared to loose dust processing. The produced metal met commercial grades FeCr800-FeCr900 specifications. Additional advantages included elimination of dust formation, reduction in fines generation during crushing of the final metal to 15%, and improved environmental performance. The developed technology represents an economically and environmentally viable solution for comprehensive recycling of ferroalloy dust waste.